Fabrication and characterization of transparent MEH-PPV/n-GaN (0 0 0 1) heterojunction devices
Özet
n-GaN/MEH-PPV thin film heterojunction diode was fabricated by depositing MEH-PPV thin film using spin-coating process on n-GaN (0 0 0 1). The junction properties were evaluated by measuring I-V characteristics. I-V characteristics exhibited well defined rectifying behavior with a barrier height of 0.89 eV and ideality factor of 1.7. The optical band gap of the MEH-PPV film using optical absorption method was found to be 2.2 eV and the fundamental absorption edge in the film is formed by the direct allowed transitions. At higher electric fields, the conductivity mechanism of the film shows a trap charge limited current mechanism. The obtained results indicate that the electronic parameters of the heterojunction diode are affected by properties of MEH-PPV organic film. © 2011 Elsevier B.V. All rights reserved.
Bağlantı
https://www.scopus.com/inward/record.uri?eid=2-s2.0-84856227882&doi=10.1016%2fj.optmat.2011.11.030&partnerID=40&md5=a7bda5ec986676d705da0775145f143bhttp://acikerisim.bingol.edu.tr/handle/20.500.12898/4979
Koleksiyonlar
DSpace@BİNGÖL by Bingöl University Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..