CdO thin films based on the annealing temperature differences prepared by sol-gel method and their heterojunction devices

Thumbnail
Tarih
2017
Yazar
Soylu, M. and Yazici, T.
Üst veri
Tüm öğe kaydını göster
Özet
Undoped CdO films were prepared on glass substrate and p-type silicon wafer using sol-gel spin coating method. The structural and optical properties of the films were investigated as a function of the annealing temperature. X-ray diffraction (XRD) patterns reveal that the films are formed from CdO with cubic crystal structure and (1 1 1) preferred orientation. It is seen that good crystallinity is due to the high annealing temperature. The surface morphology of the CdO films was found to be depending on the annealing temperature, showing cauliflower like structure. Optical band gaps for annealing temperature of 250 °C and 450 °C were found to be 2.49 eV and 2.27 eV, respectively, showing a decrease with raising temperature. Optics parameters such as extinction coefficient, refractive index, and surface-volume energy loss were determined with spectrophotometric analysis as a function of annealing temperature. CdO/p-Si heterojunction structure showed weak rectifying behavior. The diode parameters were found to be depending on annealing temperature. The results are encouraging to get better conjunction with CdO thin film component at optimize annealing temperature. © 2017 IOP Publishing Ltd.
Bağlantı
https://www.scopus.com/inward/record.uri?eid=2-s2.0-85040054782&doi=10.1088%2f2053-1591%2faa9cf8&partnerID=40&md5=b6a3d941a8e4b38eb641163fbb30e61b
http://acikerisim.bingol.edu.tr/handle/20.500.12898/4434
Koleksiyonlar
  • Scopus İndeksli Yayınlar Koleksiyonu [1357]





Creative Commons License
DSpace@BİNGÖL by Bingöl University Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..

DSpace software copyright © 2002-2016  DuraSpace
İletişim | Geri Bildirim
Theme by 
Atmire NV
 

 



| Politika | Rehber | İletişim |

sherpa/romeo

Göz at

Tüm DSpaceBölümler & KoleksiyonlarTarihe GöreYazara GöreBaşlığa GöreKonuya GöreBy TypeBu KoleksiyonTarihe GöreYazara GöreBaşlığa GöreKonuya GöreBy Type

Hesabım

GirişKayıt

DSpace software copyright © 2002-2016  DuraSpace
İletişim | Geri Bildirim
Theme by 
Atmire NV