CdO thin films based on the annealing temperature differences prepared by sol-gel method and their heterojunction devices

Abstract

Undoped CdO films were prepared on glass substrate and p-type silicon wafer using sol-gel spin coating method. The structural and optical properties of the films were investigated as a function of the annealing temperature. X-ray diffraction (XRD) patterns reveal that the films are formed from CdO with cubic crystal structure and (1 1 1) preferred orientation. It is seen that good crystallinity is due to the high annealing temperature. The surface morphology of the CdO films was found to be depending on the annealing temperature, showing cauliflower like structure. Optical band gaps for annealing temperature of 250 °C and 450 °C were found to be 2.49 eV and 2.27 eV, respectively, showing a decrease with raising temperature. Optics parameters such as extinction coefficient, refractive index, and surface-volume energy loss were determined with spectrophotometric analysis as a function of annealing temperature. CdO/p-Si heterojunction structure showed weak rectifying behavior. The diode parameters were found to be depending on annealing temperature. The results are encouraging to get better conjunction with CdO thin film component at optimize annealing temperature. © 2017 IOP Publishing Ltd.