Thermal annealing effects on I-V-T characteristics of sputtered Cr/n-GaAs diodes

Thumbnail
Tarih
2009
Yazar
Korkut, H. and Yildirim, N. and Turut, A.
Üst veri
Tüm öğe kaydını göster
Özet
Sputtered Cr/n-GaAs Schottky diodes have been prepared and annealed at 200 and 400 °C. The current-voltage (I-V) characteristics of the as-deposited and annealed diodes have been measured in the temperature range of 60-320 K with steps of 20 K. The effect of thermal annealing on the temperature-dependent I-V characteristics of the diodes has been investigated experimentally. The ideality factor and barrier height (BH) values for 400 °C annealed diode approximately remain unchanged from 120 to 320 K, and those of the as-deposited sample from 160 to 320 K. The departures from ideality at low temperatures have been ascribed to the lateral fluctuations of the BH. The BH values of 0.61 and 0.74 eV for the as-deposited and 400 °C annealed diodes were obtained at room temperature, respectively. A Richardson constant value of 9.83 A cm-2 K-2 for 400 °C annealed Schottky diode, which is in close agreement with the known value of 8.16 A cm-2 K-2 for n-type GaAs. Furthermore, T0 anomaly values of 15.52, 10.68 and 5.35 for the as-deposited and 200 and 400 °C annealed diodes were obtained from the nT versus T plots. Thus, it has been seen that the interface structure and quality improve by the thermal annealing at 400 °C. © 2009 Elsevier B.V. All rights reserved.
Bağlantı
https://www.scopus.com/inward/record.uri?eid=2-s2.0-71149100471&doi=10.1016%2fj.physb.2009.07.156&partnerID=40&md5=5e4e7cebc75ee8b8170a77c0f364afa3
http://acikerisim.bingol.edu.tr/handle/20.500.12898/5134
Koleksiyonlar
  • Scopus İndeksli Yayınlar Koleksiyonu [1357]





Creative Commons License
DSpace@BİNGÖL by Bingöl University Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..

DSpace software copyright © 2002-2016  DuraSpace
İletişim | Geri Bildirim
Theme by 
Atmire NV
 

 



| Politika | Rehber | İletişim |

sherpa/romeo

Göz at

Tüm DSpaceBölümler & KoleksiyonlarTarihe GöreYazara GöreBaşlığa GöreKonuya GöreBy TypeBu KoleksiyonTarihe GöreYazara GöreBaşlığa GöreKonuya GöreBy Type

Hesabım

GirişKayıt

DSpace software copyright © 2002-2016  DuraSpace
İletişim | Geri Bildirim
Theme by 
Atmire NV