Electrical properties and interface state energy distributions of Cr/n-Si Schottky barrier diode

Abstract

In this study, the electrical characteristics of the Cr/n-type Si (MS) Schottky barrier diode have been investigated by the current-voltage (I-V) and capacitance-voltage (C-V) measurements at 300 K temperature. Using the thermionic emission theory, the values of ideality factor and the barrier height have been obtained to be 1.22, 0.71 and 1.01, 0.83 eV, from the results of the I-V and C-V measurements, respectively. The barrier height (Φb) and the series resistance (RS) obtained from Norde's function have been compared with those obtained from Cheung functions, and a good agreement between the results of both methods was seen. The interface state density (NSS) calculated without the RS is obtained to be increasing exponentially with bias from 2.40 × 1012 cm -2 eV-1 in (EC-0.623) eV to 1.94 × 1014 cm-2 eV-1 in (EC-0.495) eV, also, the NSS obtained taking into account the RS has increased exponentially with bias from 2.07 × 1012 cm -2 eV-1 to 1.47 × 1014 cm-2 eV-1 in the same interval.